Any-Core is dual cured composite material for use in the fabrication of core build-up and post cementation.
Advantages
Optimum viscosity(Flow)&flowability
Excellent Compressive strength (330Mpa) and Flexural strength (160Mpa)
Preparation similar to Dentin
Light curing time 20sec / 2mm
Chemical curing time : 5min (intra oral)
Low polymerization shrinkage
Excellent radiopaque
Working time : 2min